First Principles Study of Defect Formation in Thermoelectric Zinc Antimonide, β-Zn4Sb3

Alireza Faghaninia, Cynthia S Lo

J Phys Condens Matter. 2015 Apr 1;27(12):125502.

PMID: 25757075

Abstract:

Understanding the formation of various point defects in the promising thermoelectric material, β-Zn(4)Sb(3), is crucial for theoretical determination of the origins of its p-type behavior and considerations of potential n-type dopability. While n-type conductivity has been fleetingly observed in Te:ZnSb, there have been no reports, to the best of our knowledge, of stable n-type behavior in β-Zn(4)Sb(3). To understand the origin of this difficulty, we investigated the formation of intrinsic point defects in β-Zn(4)Sb(3) density functional theory calculations. We found that a negatively charged zinc vacancy is the dominant defect in β-Zn(4)Sb(3), as it is also in ZnSb. This explains the unintentional p-type behavior of the material and makes n-doping very difficult since the formation of the defect becomes more favorable at higher Fermi levels, near the conduction band minimum (CBM). We also calculated the formation energy of the cation dopants: Li, Na, B, Al, Ga, In, Tl; of these, only Li and Na are thermodynamically favorable compared to the acceptor Zn vacancy over a range of Fermi levels along the band gap. Further analysis of the band structure shows that Li:Zn(4)Sb(3) has a partially occupied topmost valence band, making this defect an acceptor so that Li:Zn(4)Sb(3) is indeed a p-type thermoelectric material. The introduction of Li, however, creates a more orderly and symmetric configuration, which stabilizes the host structure. Furthermore, Li reduces the concentration of holes and increases the Seebeck coefficient; hence, Li:Zn(4)Sb(3) is more stable and better performing as a thermoelectric material than undoped β-Zn(4)Sb(3).

Chemicals Related in the Paper:

Catalog Number Product Name Structure CAS Number Price
AP12039428 Zinc antimonide Zinc antimonide 12039-42-8 Price
qrcode