Influence of Fluoride in poly(d,l-lactide)/apatite Composites on Bone Formation

Influence of Fluoride in poly(d,l-lactide)/apatite Composites on Bone Formation

X Luo, D Barbieri, G Passanisi, H Yuan, J D de Bruijn

J Biomed Mater Res B Appl Biomater. 2015 May;103(4):841-52.

PMID: 25132540

Abstract:

The influence of fluoride in poly(d,l-lactide)/apatite composites on ectopic bone formation was evaluated in sheep. Nano-apatite powders with different replacement levels of OH groups by fluoride (F) (0% (F0), 50% (F50), 100% (F100), and excessive (F200)) were co-extruded with poly (d,l-lactide) at a weight ratio of 1:1. Fluoride release from the composites (CF0, CF50, CF100, and CF200) was evaluated in vitro and bone formation was assessed after intramuscular implantation in sheep. After 24 weeks in simulated physiological solution, CF0 and CF50 showed negligible fluoride release, whereas it was considerable from the CF100 and CF200 composites. Histology showed that the incidence of de novo bone formation decreased in implants with increasing fluoride content indicating a negative influence of fluoride on ectopic bone formation. Furthermore, a significant decrease in resorption of the high fluoride-content composites and a reduction in the number of multinucleated giant cells were seen. These results show that instead of promoting, the presence of fluoride in poly(d,l-lactide)/apatite composites seemed to suppresses their resorption and osteoinductive potential in non-osseous sites.

Chemicals Related in the Paper:

Catalog Number	Product Name	Structure	CAS Number	Price
AP26680104-C	Poly(D,L-lactide)		26680-10-4	Price

As a specialist in analytical chemical Products, Alfa Chemistry offers consumers a wealth of raw materials and a full range of technologies and services.

QUICK LINKS

HEADQUARTERS

Tel:

Fax:

Email: