Porous Calcium Polyphosphate Scaffolds for Bone Substitute Applications -- In Vitro Characterization

Porous Calcium Polyphosphate Scaffolds for Bone Substitute Applications -- In Vitro Characterization

R M Pilliar, M J Filiaggi, J D Wells, M D Grynpas, R A Kandel

Biomaterials. 2001 May;22(9):963-72.

PMID: 11311015

Abstract:

Porous structures were formed by gravity sintering calcium polyphosphate (CPP) particles of either 106-150 or 150-250 microm size to form samples with 30-45 vol% porosity with pore sizes in the range of 100 microm (40-140 microm). Tensile strength of the samples assessed by diametral compression testing indicated relatively high values for porous ceramics with a maximum strength of 24.1 MPa for samples made using the finer particles (106-150 microm). X-ray diffraction studies of the sintered samples indicated the formation of beta-CPP from the starting amorphous powders. In vitro aging in 0.1 M tris-buffered solution (pH 7.4) or 0.05 M potassium hydrogen phthalate buffered solution (pH 4.0) at 37 degreesC for periods up to 30d indicated an initial rapid loss of strength and P elution by 1 d followed by a more gradual continuing strength and P loss resulting in strengths at 30d equal to about one-third the initial value. The observed structures, strengths and in vitro degradation characteristics of the porous CPP samples suggested their potential usefulness as bone substitute materials pending subsequent in vivo behaviour assessment.

Chemicals Related in the Paper:

Catalog Number	Product Name	Structure	CAS Number	Price
AP877247	Potassium phthalate monobasic		877-24-7	Price

As a specialist in analytical chemical Products, Alfa Chemistry offers consumers a wealth of raw materials and a full range of technologies and services.

QUICK LINKS

HEADQUARTERS

Tel:

Fax:

Email: