Synthesis and Characterization of a Poly(dimethylsiloxane)-Poly(ethylene Oxide) Block Copolymer for Fabrication of Amphiphilic Surfaces on Microfluidic Devices

Synthesis and Characterization of a Poly(dimethylsiloxane)-Poly(ethylene Oxide) Block Copolymer for Fabrication of Amphiphilic Surfaces on Microfluidic Devices

Scott A Klasner, Eve C Metto, Gregory T Roman, Christopher T Culbertson

Langmuir. 2009 Sep 1;25(17):10390-6.

PMID: 19572528

Abstract:

A poly(dimethylsiloxane)-poly(ethylene oxide) (PDMS-PEO) vinyl terminated block copolymer has been synthesized via a simple hydrosilylation reaction between hydride-terminated PDMS and PEO divinyl ether. This prepolymer can be subsequently cross-linked into an elastomer in a second hydrosilylation reaction involving a methylhydrosiloxane-dimethylsiloxane copolymer, forming a material suitable for the purposes of fabricating microfluidic devices. The presence of the PEO block in the prepolymer chain results in a much more hydrophilic material following cross-linking. The surface water contact angle of the PDMS-PEO material is 65 degrees +/- 3 (n = 6), as opposed to approximately 110 degrees for native PDMS. Droplets of water straddled by air within molded channels of the PDMS-PEO are concave in shape with contact angles where the fluid meets the side walls of 32 degrees +/- 4 (n = 8), while droplets in PDMS microchannels are more convex with contact angles of 95 degrees +/- 6 (n = 6). The length of the PDMS-PEO prepolymer chain and the multifunctional hydride cross-linker chains appear to dictate the durability of the elastomeric material. Young's modulus measurements yielded values of 0.94 +/- 0.08, 2.6 +/- 0.8, and 1.91 +/- 0.06 MPa for a [5% vinyl excess prepolymer and 10-fold excess of cross-linker], [10% vinyl excess prepolymer and 5-fold excess of cross-linker], and 10:1 PDMS, respectively, confirming that the elasticity of the cross-linked PDMS-PEO is similar to that of PDMS (Sylgard 184:10:1 mixture of elastomeric base to elastomer curing agent). The PDMS-PEO material still possesses enough PDMS character to allow molded channel architectures to be sealed between two pieces of the block copolymer by conformal contact. As a result of the more hydrophilic nature of the material, the channels of devices fabricated from this polymer are self-filling when using aqueous buffers, making it more user-friendly than PDMS for applications calling for background electrolytes void of organic modifiers. Different compositions of PDMS-PEO devices feature different electroosmotic flow values with the 5% vinyl excess prepolymer EOF values of 2.5 +/- 0.7 x 10(-4) and 5.7 +/- 0.8 x 10(-4) cm(2)/(V s) at pHs 6 and 9, respectively, and 1.2 +/- 0.3 x 10(-4) and 2.5 +/- 0.3 x 10(-4) cm(2)/(V s) for the 10% vinyl excess prepolymer device at pHs 6 and 9, respectively.

Chemicals Related in the Paper:

Catalog Number	Product Name	Structure	CAS Number	Price
AP68951962	Poly(dimethylsiloxane-co-diphenylsiloxane), divinyl terminated		68951-96-2	Price

As a specialist in analytical chemical Products, Alfa Chemistry offers consumers a wealth of raw materials and a full range of technologies and services.

QUICK LINKS

HEADQUARTERS

Tel:

Fax:

Email: